国际上GCC、NEXANS、CCI、JINRO、PIRELLI等公司生产石油平台电缆的厂家,在耐泥浆电缆护套的性能要求上,基本上均按照NEK606标准考核。主要是在IEC 60092-359 的SHF2型的基础上,加上了耐泥浆要求,如耐IRM903油,100℃7天,要求抗张强度、断裂伸长率、体积膨胀、重量增加均≤30%。我一直在寻求此料,但至尽收获很小,国内常规的无卤料(无论辐照交联、还是蒸汽硫化)指标相距很大,特别是后两项指标。各位理工朋友如果对这方面有过研究的,请指点或探讨。
[copartner 在 2007-12-19 13:54:39 编辑过]
fxmeng --- 2007-03-19 10:46:30
2
一般的聚烯烃无卤料可能很难达到你的要求,建议使用PVDF。你也可以把性能要求给我,我看能不能找到你要的材料。
[echoo 在 2008-12-2 16:00:35 编辑过]
阿蓉曼薇 --- 2008-12-02 14:31:26
3
SFC --- 2008-12-03 13:19:22
4
也许我们可以帮到诸位!
NEK606对于国内的目前的标准来说,就是耐油、耐泥浆的要求高一些!
可以通过干式硅烷交联或通过辐照交联以获得更高的耐温性能。
DESCRIPTION/FEATURES: Low Smoke Fume Zero Halogen Compound (LSFOH)
APPLICATIONS: Wire & Cable
Physical properties Test method Unit Typical value
Specific density ISO 1183 kg/m3 1510
Melt flow, 150°C , 21,6 kg ISO 1133, (b) g/10min 2,5
Tensile strength IEC 60811-1-1 MPa 9 (12**)
Elongation at break IEC 60811-1-1 % 180(160**)
Tear strength BS 6469:99.1 N/mm 6
Hot pressure test 6h at 115°C IEC 60811-3-1 % 8
Hot pressure test 4h at 125°C IEC 60811-3-1 % 34**
Cold impact at -40°C IEC 60811-1-4 pass
Elongation at break -40°C IEC 60811-1-4 % 40
Air ageing 10d at 120°C
Tensile strength, variation from original % -26 (25**)
Elongation, variation from original % -40 (-16**)
** After Crosslinking
Burning properties Test method Unit Typical value
Oxygen index ISO 4589-2 % 34 *
Flammability temperature index ISO 4589-3 °C 330**
Smoke density – Flaming mode (1mm) ASTM E-662 Ds max -
Smoke density – Non Flaming Mode (1mm) ASTM E-662 Ds max -
Toxicity NES 713 - -
Halogen content IEC 60754-1 - *
Acid Gas Emission IEC 60754-2 -
- pH (min) pH 4.34
- conductivity (max) μScm-1 21.5
*measured on type IV specimen
**measured on type II specimen
Electrical properties Test method Unit Typical value
Dielectric constant at 50 Hz, at 23°C, 50%HR IEC 60250 4.01
Dissipation factor at 50 Hz, at 23°C, 50%HR IEC 60250 0.001
Dissipation factor at 1MHz, at 23°C, 50%HR IEC 60250 0,07
Volume resistivity , at 23°C, 50%HR IEC 60093 W cm 3,2x 1015
Surface resistivity , at 23°C, 50%HR IEC 60093 W 3,0x 1015
Other properties Test method Unit Typical value
Water absorption after 7d at 70°C BS 6724 mg/cm2 1,43
Tensile strength, variation from original % 2 (-5**)
Elongation, variation from original % -45 (-11**)
Oil ageing, IRM 902 oil, 7d at 100°C IEC 60811-2-1
Tensile strength, variation from original % -10 (-8**)
Elongation, variation from original % -21 (-21**)
Oil ageing, IRM 903 oil, 7d at 100°C IEC 60811-2-1
Tensile strength, variation from original % -35 (-28**)
Elongation, variation from original % -40 (-21**)
Mud resistance, oil based, 56d at 70°C IEC60892-4 (NEK606)
Tensile strength, variation from original % -7(-19**)
Elongation, variation from original % -44 (-32**)
** After Crosslinking
Heat shock 1h at 150°C IEC 60811-3-1 Pass
Hardness ISO R 868 Shore D 48
Hardness ISO R 868 Shore A 94
Mooney viscosity, ML (1+4) 140°C DIN 53523 - 58
Shrinkage, 1h at 100°C IEC 60811-1-3 % 0
gaojun --- 2009-03-27 14:53:45
5
楼上能否告知具体的联系方式
crazylyj --- 2009-03-29 17:35:02
6
国内现在又可以做到的厂家,上海好像有一家的。不过听说比从韩国进口的护套聊SHF MUD还要贵,如此就不如进口了
SFC --- 2009-04-03 11:15:40
7
这种材料是欧洲的产品,有很多成功案例!
但是 进口成本实在太高 可能要100多元/kg,而在欧洲可能就3、5欧元/kg.
NEK 606里的 耐泥浆试验 对泥浆的要求有标准,不同地区的泥浆不一样,挪威的标准 用中国的泥浆肯定不行。
当然 很多厂商的线缆 在耐温和耐油方面性能还是不好,强度也不高!
阻燃要求反而不高,但这种材料还用MTH +EVA的阻燃机理!
也就是说 我们国内其实完全可以做这种材料,只是缺乏经验可市场!
befut --- 2009-04-03 12:11:29
8
中国的海上石油平台电缆主要按照哪个标准?
gaojun --- 2009-09-05 08:20:56
9
我已做了几种料能满足SHF Mud 护套的要求,而且,产品取得了DNV的型式认可证书。现在唯一需要进一步研究的是“泥浆”,相信各海域的“泥浆”成份是不同的。检测只是采用代表性的钻井液体,不能真正代表实际使用环境的考验。
za8373 --- 2009-11-16 17:55:55
10
孟魂 --- 2009-11-27 10:58:01
11
edwardtom --- 2010-08-21 08:18:51
12
英文版的有,网上可以下到
edwardtom --- 2010-08-21 08:22:13
13
edwardtom --- 2010-08-21 08:27:44
14
guleilei07 --- 2010-09-13 15:58:49
15
majinqiang --- 2011-08-31 10:33:15
16
g923yf --- 2011-09-19 16:40:42
17
DSM --- 2011-09-21 23:51:14
18